Product Details:
|
| Application: | Thin Film And Thick Film Microelectronic , High Power And High Frequency Circuit RF / Microwave Components And Capacitor Or Resistor | Diameter: | Ø 1" / Ø 2" / Ø 3" / Ø 4" |
|---|---|---|---|
| Thickness: | 0.4 Mm / 0.5 Mm / 1 Mm | Grade: | SAW Grade And Optical Grade |
| Highlight: | 1" Zirconia Ceramic Substrate,ZrO2 Zirconia Ceramic Substrate,2" Zirconia Ceramic Substrate |
||
ZrO2 ( zirconia ) ceramic substrate
We provides ZrO2 ( zirconia ) ceramic substrate . ZrO2 substrate is one of the most popular ceramic substrate which has excellent heat resistance, high mechnical strength , abrasion resistance and small dielectric loss . The surface of ZrO2 substrate is quite smooth and low porosity . Compared to alumina substrate , ZrO2 substrate has higher mechanical strength and fracture toughness , it's about three times higher for bending strength, two times for fracture toughness than alumina substrate . ZrO2 substrate ( zirconia ) also provides good abrasion resistance. It features a thermal expansion rate close to metals . SWI provides ZrO2 ceramic substrates for a wide range of applications, including thin film and thick film microelectronic , high power and high frequency circuit RF / microwave components and capacitor or resistor , contact us for more ceramic wafer product information .
| Chemical formula | ZrO2 |
| Color | white |
| Density | 6.04 g/cm 3 |
| Thermal conductivity | 2.4 W/m. K |
| Thermal Expansion ( x10 -6 / ℃ ) | 10 |
| Dielectric strength | 14E6 |
| Dielectric Constant (at 1MHZ) | 29 |
| Loss Tangent (x10 -4 @1MHZ) | 0.001 |
| Volume Resistivity | >1E14 ohm-cm |
| Diameter | Ø 1" / Ø 2" / Ø 3" / Ø 4" |
|---|---|
| Square size | 10 x 10 / 20 x 20 / 50 x 50 / 100 x 100 mm |
| Thickness | 0.4 mm / 0.5 mm / 1 mm |
| Surface | As fired |
| one side polished / two sides polished | |
| Roughness | Ra <= 0.3 um |